Plasma Spraying
Plasma spraying is suitable for most cobalt, nickel and iron base alloys, plus a very wide range of ceramics, composites and carbides. The process may be used on most materials, which can be prepared by grit blasting. Deposits are thin (0.1mm to 0.2mm), high density (approaching 99% with the newer high energy plasma equipment), and since the substrate is only slightly heated, can be applied with a minimum of distortion. However, the coatings are not fusion welded overlays, and are only mechanically bonded to the substrate.
Quality Level: As per National Standard & International Standards.
Sizes available: Dia.50mm--1500mm.
Application Field: Mining Industry, Valve and Pump Industry,Heat-treatment Industry, Metallurgical Industry, Cement Industry,Power plants, Oil, Gas Industry.
Material Grade:
| Metal No: | Chemical Compostion(W%) |
| C | Si | Cr | Mo | Mn | Fe | Cu | Ti | Ai | Ni |
| Ni200Z | 1.00 | 2.00 | -- | -- | 1.50 | 3.00 | 1.25 | -- | -- | Bal |
| Ni202Z | 0.15 | 3.30 | -- | -- | -- | -- | -- | B2.3 | -- | Bal |
| Ni205Z | 0.12 | 1.00 | 16.50 | 17.00 | 1.00 | 6.50 | -- | W:4.50 | V:0.30 | Bal |
| Ni206Z | 0.12 | 1.00 | 1.00 | 28.00 | 1.00 | 5.00 | -- | -- | V:0.40 | Bal |
| Ni207Z-NZ | -- | 1.20 | 25.00 | 11.00 | -- | -- | -- | -- | -- | Bal |
| Ni219Z | -- | -- | 12.70 | 9.00 | -- | -- | Be
2.0 | 0.4 | 2 | Bal |
| Ni222Z | -- | 0.50 | 22.00 | 13.00 | 0.70 | 4.00 | | -- | -- | Bal |
| Ni230 | 0.30 | 1.50 | -- | -- | 1.50 | 3.50 | 30.00 | Nb:2.00 | -- | Bal |
| Ni235 | 0.35 | 2.00 | -- | -- | 1.50 | 3.50 | 30.00 | Nb:0.50 | -- | Bal |
| Ni240Z | 0.35 | 1.25 | -- | -- | 1.50 | 3.50 | 29.50 | Nb:0.50 | -- | Bal |
| Ni250Z | 0.12 | 0.30 | -- | -- | 1.50 | 2.00 | 27-33 | 0.60 | 3.00 | 68.00 |
| Ni255 | 0.05 | 0.50 | 12.50 | 3.00 | 1.50 | 1.70 | bi:4.00 | sn:4.00 | -- | Bal |
| Ni260Z | 0.40 | 3.00 | 15.5 | -- | 1.50 | 11.00 | -- | -- | -- | Bal |
| Ni262Z | 0.06 | 1.00 | 21.5 | 9.5 | 1.00 | 5.00 | -- | Nb:4.00 | -- | Bal |
| Ni264 | 0.03 | -- | 60.00 | -- | -- | 0.40 | -- | -- | -- | Bal |
| Ni274Z | 0.02 | 0.80 | 16.00 | 16.5 | 1.00 | 2.00 | -- | W:1.00 | -- | Bal |
| Ni278Z | 0.08 | 0.35 | 19.00 | 3.00 | 0.35 | Bal | 0.30
Co:1.00 | 0.90
Nb:5.00 | 0.60 | 53.00 |
Production Process
Step 1: Getting orders.
Step 2: Process design by technical department
Step 3: Purchase of raw materials and pattern making &checking
Step 4: Inspection of raw materials
Step 5: Melting by middle-frequency induction furnaces
Step 6: Ladle analysis by Spectrometer
Step 7: De-oxidization, slag-removal, tapping
Step 8: Pouring
Step 9: Openning & fettling
Step 10: Surface & dimensional check
Step 11: Heat treatment
Step 12: Inspection of physical property (UT test,MT test, hardness,impact value µstructure)
Step 13: Packing
Step 14: Shipping
1. 18-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication.
3. Professional Export Practices: Have Exported to +60 Overseas Countries.
Our Trade Show 
Our booth No. 14-A29-5 in Newcast 2015,Germany
Hall 14, Stand No.A29-5.
Contact Us for further information about products & service:
Mr.John Liu
Project Manager
Cell: 0086-130 930 23772(What's App)
Tel: 0086-188 0059 6372
Fax: 0086-510-6879 2172
E-mail: cast@ebcasting.com； ebcastings@163.com
Skype ID:julia.zhu26
QQ: 217 039 6403
www.ebcastings.com
Eternal Bliss Alloy Casting & Forging Co.,LTD.
Add.: J-Sci-Tech Park, Binhu District,Wuxi,214122, Jiangsu,China