The commercial forms of nickel and nickel-base alloys are fully austenitic and are used/selected mainly for their resistance to high temperature and aqueous corrosion.
Commercially Pure and Low-Alloy Nickels. Nickel is supplied to the producers of nickel alloys in powder, pellets, or anode forms. This has led to a whole series ofalloy modifications, with controlled compositions having nickel contents ranging from about 94% to virtually 100%.
Quality Level: As per National Standard & International Standards.
Sizes available: As per your drawings.
Application Field: Valve Seat, bearing sleeve,pump shaft,seeling ring,wear gaskt,bearing bush,hot extruding dies,steam turbine blade,food processing industry,valve gate,valve board,valve seat ring,dental industry.
Material Grade:
| Metal No: | Chemical Compostion(W%) |
| C | Si | Cr | Mo | Mn | Fe | Cu | Ti | Ai | Ni |
| Ni200Z | 1.00 | 2.00 | -- | -- | 1.50 | 3.00 | 1.25 | -- | -- | Bal |
| Ni202Z | 0.15 | 3.30 | -- | -- | -- | -- | -- | B2.3 | -- | Bal |
| Ni205Z | 0.12 | 1.00 | 16.50 | 17.00 | 1.00 | 6.50 | -- | W:4.50 | V:0.30 | Bal |
| Ni206Z | 0.12 | 1.00 | 1.00 | 28.00 | 1.00 | 5.00 | -- | -- | V:0.40 | Bal |
| Ni207Z-NZ | -- | 1.20 | 25.00 | 11.00 | -- | -- | -- | -- | -- | Bal |
| Ni219Z | -- | -- | 12.70 | 9.00 | -- | -- | Be
2.0 | 0.4 | 2 | Bal |
| Ni222Z | -- | 0.50 | 22.00 | 13.00 | 0.70 | 4.00 | | -- | -- | Bal |
| Ni230 | 0.30 | 1.50 | -- | -- | 1.50 | 3.50 | 30.00 | Nb:2.00 | -- | Bal |
| Ni235 | 0.35 | 2.00 | -- | -- | 1.50 | 3.50 | 30.00 | Nb:0.50 | -- | Bal |
| Ni240Z | 0.35 | 1.25 | -- | -- | 1.50 | 3.50 | 29.50 | Nb:0.50 | -- | Bal |
| Ni250Z | 0.12 | 0.30 | -- | -- | 1.50 | 2.00 | 27-33 | 0.60 | 3.00 | 68.00 |
| Ni255 | 0.05 | 0.50 | 12.50 | 3.00 | 1.50 | 1.70 | bi:4.00 | sn:4.00 | -- | Bal |
| Ni260Z | 0.40 | 3.00 | 15.5 | -- | 1.50 | 11.00 | -- | -- | -- | Bal |
| Ni262Z | 0.06 | 1.00 | 21.5 | 9.5 | 1.00 | 5.00 | -- | Nb:4.00 | -- | Bal |
| Ni264 | 0.03 | -- | 60.00 | -- | -- | 0.40 | -- | -- | -- | Bal |
| Ni274Z | 0.02 | 0.80 | 16.00 | 16.5 | 1.00 | 2.00 | -- | W:1.00 | -- | Bal |
| Ni278Z | 0.08 | 0.35 | 19.00 | 3.00 | 0.35 | Bal | 0.30
Co:1.00 | 0.90
Nb:5.00 | 0.60 | 53.00 |
Production Process
Step 1: Getting orders.
Step 2: Process design by technical department
Step 3: Purchase of raw materials and pattern making &checking
Step 4: Inspection of raw materials
Step 5: Melting by middle-frequency induction furnaces
Step 6: Ladle analysis by Spectrometer
Step 7: De-oxidization, slag-removal, tapping
Step 8: Pouring
Step 9: Openning & fettling
Step 10: Surface & dimensional check
Step 11: Heat treatment
Step 12: Inspection of physical property (UT test,MT test, hardness,impact value µstructure)
Step 13: Packing
Step 14: Shipping
1. 16-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication.
3. Professional Export Practices: Have Exported to +60 Overseas Countries.
Our Trade Show 
Our booth No. 14-A29-5 in Newcast 2015,Germany
Hall 14, Stand No.A29-5.
Contact Us for further information about products & service:
Mr.John Liu
Project Manager
Cell: 0086-130 930 23772(What's App)
Tel: 0086-188 0059 6372
Fax: 0086-510-6879 2172
E-mail: cast@ebcasting.com； ebcastings@163.com
Skype ID:julia.zhu26
QQ: 217 039 6403
www.ebcastings.com
Eternal Bliss Alloy Casting & Forging Co.,LTD.
Add.: J-Sci-Tech Park, Binhu District,Wuxi,214122, Jiangsu,China